    d.SIGN 67

    Product Number: #B601084
    d.SIGN 67 5 g 579914
    31g 579916

    d.SIGN 67

    d.SIGN 67 is a palladium-based ceramic alloy. The high heat resistance and the excellent melting and flow properties enable easy processing up to polishing.

    Indications:

  • Onlays, 3/4 crowns, crowns
  • Telescope crowns, conus crowns
  • Bridges
  • Wide-span bridges
  • Cast posts / cores, bars, attachments
  • Implant-supported superstructures
  • Partial dentures
  •  

    Advantages:

  • Good melting and flow properties
  • Easy processing and polishing
  • Compatible with conventional metal-ceramics (eg IPS Style)
  • Wide range of indications
  • Certified biocompatibility
  •  

     Composition (%):  Pd 62.7 | Ag 20.0 | Au 4.0 | Sn 10.0 | In 1.5 | Ga 1.7 | Ru < 1.0 , Re < 1.0, Li < 1.0       
     ISO  22674 : 2016
     ADA Class:  Noble
     Type / Color:  4 / White
     Density (g/cm3)  10.8
     Melting Range (Solidus / Liquidus):     1150 - 1270 C
     Elastic Modulus (GPa):  135
     . Porcelain Fired    Hardened   
     Vickers Hardness:  245 290
     Tensile Strength (Mpa):    785 840
     0.2% Proof Stress (MPa):    545 595
     Elongation (%):  12 10
     Investment Material:  Phosphate - bonded
     Preheating / Burn-out Temperature:     750 - 820 C
     Crucible  Ceramic crucible
     Casting Temperature:  1325 - 1385 C
     Oxidation C / Min / Vacuum:  1950 / 1 / No
     CTE:  (25 - 500 C): 13.9 x 10-6 / K
     Recommended Metal Ceramic:  IPS Style, IPS InLine One, IPS InLine, IPS Classic, IPS d.SIGN   
     Laser Welding Wire:  Laser Ceramic White